FILM DESCRIPTION |
|
Non heat sealable, one side treated coextruded biaxially
oriented polypropylene transparent film, suitable for: |
|
Rotogravure and flexographic printing.
|
|
Lamination with other films or with paper.
|
| |
|
CHARACTERISTICS |
|
Excellent transparency and gloss.
|
|
Excellent ink adhesion on treated side.
|
|
High resistance to oil, grease, chemicals, puncture and
abrasion.
|
|
Good barrier to moisture, odours and gases.
|
|
Non heat sealable film.
|
| |
|
APPLICATIONS |
|
Food packaging (biscuits, pasta, snacks, chips and bread).
|
|
Non – food packaging (textile sacks and floers).
|
|
|
Properties |
unit |
Test method |
Tolerance |
Typical value |
|
Thickness |
micron |
-- |
±3% |
15 |
20 |
25 |
30 |
35 |
40 |
|
Yield |
m²/ kgm |
-- |
±3% |
73.3 |
55 |
44 |
36.6 |
31.5 |
27.5 |
| Unit weight |
gm/m² |
-- |
±3% |
13.7 |
18.2 |
22.8 |
27.3 |
31.9 |
36.4 |
|
|
N/mm² |
ASTM D 882 |
|
|
120 |
120 |
120 |
120 |
120 |
120 |
|
240 |
240 |
240 |
240 |
240 |
240 |
|
|
Breaking
elongation |
MD |
|
TD |
|
% |
ASTM D 882 |
|
|
160 |
160 |
160 |
160 |
160 |
162 |
|
50 |
50 |
50 |
50 |
50 |
50 |
|
|
Modulus of
elasticity |
MD |
|
TD |
|
N/mm² |
ASTM D 882 |
|
|
2000 |
2000 |
2000 |
2000 |
2000 |
2000 |
|
3400 |
3400 |
3400 |
3400 |
3400 |
3400 |
|
|
|
% |
In air, in oven
For 5 min.
At 130 ºC |
|
|
| Haze |
% |
ASTM D 1003 |
Max. |
2 |
2 |
2 |
2 |
2 |
2 |
| Gloss |
G.U. |
ASTM D 2457 |
Min. |
90 |
90 |
90 |
90 |
90 |
90 |
| Coefficient of
friction |
-- |
ASTM D 1894 |
± 0.05 |
0.35 |
0.35 |
0.35 |
0.35 |
0.35 |
0.35 |
| Water vapour
permeability |
g/m².24 hrs
at 38 ºC
90% RH |
ASTM E
96-66
BS 3177 |
Max. |
10.7 |
8.3 |
6.6 |
5.5 |
4.7 |
4.1 |
| Oxygen
permeability |
cc/m². 24hrs
Bar, at 23ºC,
0% RH |
ASTM D
1434
Bs 2782 –
514 A |
Max. |
2700 |
2200 |
1800 |
1500 |
1300 |
1100 |
| Wetting tension |
dyne/cm |
ASTM D 2578 |
± 20 |
40 |
40 |
40 |
40 |
40 |
40 |
| Denisty |
Kgm/m³ |
ASTM D 1505 |
± 0.05 |
0.91 |
0.91 |
0.91 |
0.91 |
0.91 |
0.91 |
|
|